Material: PLA-HI Filament 2,85mm,
Packing unit: each 0,75 kg material plus coil
Should your country not be selectable during checkout, please send an e-mail to email@example.com
1 Item Items
Warning: Last items in stock!
BIOBASED 3D-PRINTING FILAMENT WITH HIGH IMPACT STRENGTH AND ACCURATE PRINTING QUALITY
CREAMELT® PLA-HI is a biiobased 3D printing filament with high impact strength. It is made from natural resourced PLA (Polyactic Acid), which is additionally modified with impact modifier that makes it more impact resistant rather than most other PLA on the market.
PLA-HI is easy to print with and gives accurate measure-ments due to minimal shrinkage of the material when cooling down. It has interesting mechanical properties, good layer adhesion and wokrs with most 3D printers on the market.
CREAMELT® PLA-HI gives you the ability to print functional parts with smooth surfaces and high impact resistance.
PRINTING TEMPERATURE = 200...220 °C
PLATFORM TEMPERATURE = 50...60 °C
PRINT SPEED = 40...150 mm/s
TENSILE MODULUS = 2440 MPa
TENSILE STRENGTH = 40 MPa
TENSILE STRAIN AT BREAK = 8...13 %
IMPACT STRENGTH = 80 kJ/m^2 (ISO 179 / 1eU CHARPY)
SHORE HARDNESS = -
* as measured by printed tensile bars at 23°C
PHYSICAL& THERMAL PROPERTIES
DENSITY = 1240 kg/m^3
MELTING POINT = 145...160 °C
GLASS TRANSITION POINT = 55...60 °C